Decription
Liquid rubber coating material is the keymaterial of silicon PU material, which is composed of two-component PU materialand material containing silicone composition. Effectively solve the PU materialsin the professional performance, environmental protection construction, life,routine maintenance and other aspects of the lack.
Structure
Feature
Self-leveling, have a good shock absorptionand resilience, anti-skid, strong anti-fouling, one component moisture curing,construction is simple, simple maintenance, environmental performance.
Technical Data
Item | Data |
Shape | Light green color liquid |
Viscosity(25℃,Mpa·s) | 4000~10000 |
Solidity(%) | ≥ 92 |
Applicableperiod(25℃,min) | ≥ 40 |
Surface curing time(25℃,h) | ≤ 8 |
Full curing time(25℃,h) | ≤ 12 |
Hardness Shore A | 40~50 |
Tensilestrength(MPa) | ≥ 1.5 |
Elongation at break(%) | ≥ 450 |
Compression recoveryrate(%) | ≥ 24 |
Package and Storage
Packing: 30kg/ drum
Upside down stored.
Stored in a cool, ventilated and dry warehouse,keep away from fire and heat sources, and keep waterproof, damp proof and lightproof.
Storage period: six months from the date ofproduction. More than the storage period, the test can continue to use.
Composition
Chemical Name | In % by Weight | CAS No. | EC No. | Molecular Formula |
polyurethane resin | 32% | 9009-54-5 | 210-898-8 | C3H8N2O |
DOTP | 13% | 6422-86-2 | 229-176-9 | C24H38O4 |
Calcium carbonate | 25% | 471-34-1 | 207-439-9 | CaCO3 |
Talc | 15% | 14807-96-6 | 238-877-9 | Mg3[Si4O10](OH)2 |
iron oxide | 10% | 1332-37-2 | 215-570-8 | ----- |
Urea formaldehyde | 5% | 9011-05-6 | ----- | C2H6N2O2 |
Installation
1) At least apply2layers or 2.7mm
2) Usage: (1layer use0.7—1mm/㎡)
0.7mm/㎡ usage is 1.2-1.3kg
1mm/㎡ usage is 1.4-1.5kg
3) 30kg liquid rubbercoating material mix with 0.9—1.2kg PU resin and 100-180gram water, applied byrubber squeegee
4) After 1 layer, itshould maintain about 10-12 hours, ensure the firstly layer are dry, then thenext process.
5)Wheninstall the firstly layer on concrete base ,we suggest 30kg liquid rubber coatmaterial mix with 180gram silica sand .(It is better to seal the sub-base moistures)